Investment Powder > STANDARD
JPL Standard is competitive and aid casters in the most demanding of casting environments. JPL Standard can support caster in terms of minimize the cost of jewelry production, while produces casting with the superior surfaces which re-ducing metal loss to full minimum.
JPL Standard can satisfyingly cast Silver, Brass and Bronze Alloys with smooth surface finish, and also suit-able for centrifugal and Vacuum Casting Machine.
Product Packaging:
DRUM: 45.4 kg. (100 lb.)
SACK: 22.7 kg. (50 lb.)
Technical Data
POWDER / WATER RATIO WORKING TIME GLOSS OFF TIME THERMAL EXPANSION AT 750 SETTING EXPANSION AFTER 2 HOURS VOLUME YIELD PER KG. OF POWDER |
100/38-40 7-8 min. 12-14 min. 0.82% 0.57% 770 ml. |
DEWAX CYCLE
SILK CAST Yellow can be both dry and steam dewaxed with excellent results. As a general rule the larger the flask the longer the dewax time.
Dry dewax in a furnace should take place at about 175-200oC depending on the size of the flask. For a 6”x4” flash, 60-90 min will be sufficient to remove the bulk of the wax and 2 hours should be sufficient for steam dewax.
BURNOUT CYCLE
Burnout cycles will depend very much on the size of the flask. The larger the flask or the waxes therein the longer and more gradual the burnout must be. For 6”x4” flash will only need 7 hours. In addition the furnace must have a good supply of air in order to achieve a clean burnout. Carbon deposits from the wax must combine with oxygen to form CO2 and thus escape through the pores of the investment. If after Burnout your flash is a gray colour you need to get more air into the furnace-do not increase the temperature, this will only damage the investment.
CASTING
After completion of burnout, the flask should decrease flask temperature to proper casting temperature cool to proper casting temperature. The flask can then be cast by either centrifugal or vacuum casting methods.
Temperature of the last 1-2 hours of burnout must be adjusted at proper temperature for casting. If held for less than 1 hour, the core of the flasks will be at a much higher temperature, and may result in metal mould reaction in addition 15 minute is recommend time for quenching
CASTING CONDITIONS:
Metal Casting (oC) | Flask (oC) | |
Normal casting | 990 - 1000 | 550 - 580 |
Fine Filigree | 1010 - 1020 | 600 - 630 |
The above conditions are for guidance only and may need to be optimized for your own experience and knowledge of your casting machine.
Copyright © 2013 Jewelry Plaster. All Rights Reserved.
322/5-6 1st Floor, Bangkok Gem & jelelry Tower Surawong Road, Bangrak Bangkok 10500 Thailand
Tel: 02-2671178, Fax: 02-2671178, Email: jpl@jewelryplaster.com